- Home
- Products and Services
- Cement
- Product
Products and Services
- Cement
-
Metallurgy
-
Product
- Blast Furnace Ceramic Cup Series Shaped Products
- Blast Furnace Ceramic Cup Corundum-Silicon Nitride Precast Series Products
- Blast Furnace Ceramic Cup Supporting Slurry Series Products
- Blast Furnace Rapid Repair and Long-Life Series Products
- Refractory Materials for Blast Furnace Taphole
- Belt Roasting Machine Pellet Series Supporting Products
- Grate-Rotary Kiln Pellet Series Supporting Products
- Solutions
-
Product
- Environmental Protection
- Energy
- Aerospace
- Refractory Raw Materials
- Home
- Products and Services
- Cement
- Product
- Rotary Kiln
- Magnesia Alumina Zirconia...
Magnesia Alumina Zirconia Brick
【Product brand】TD-MAZ
【Recommended use】Rotary Kiln Transition Zone
Product Introduction
The Magnesia Alumina Zirconia Brick is primarily made from high-purity magnesia, magnesia-alumina spinel, and zirconia-containing raw materials, formed under high pressure and fired at high temperatures. Compared to magnesia-alumina spinel bricks, it offers superior resistance to cement clinker erosion, excellent kiln coating formation, and good thermal shock stability. It is particularly suitable for being used in the transition and burning zones of cement kilns with co-processing capabilities, with a service life exceeding 12 months.
Products Quality
|
Product Name
|
Magnesia Alumina Zirconia Brick
|
|
|
Product Code
|
TD-MAZ |
|
|
Chemical Composition (%)
|
MgO |
≥85 |
|
|
Al2O3 |
≥8 |
|
|
ZrO2 |
≥1 |
|
|
SiO2 SiO₂ |
≤0.8 |
|
Bulk Density (g/cm³)
|
≥2.90 |
|
|
Apparent Porosity (%)
|
≤17 |
|
|
Cold Crushing Strength (MPa)
|
≥60 |
|
|
Refractoriness Under Load T0.6 (°C)
|
≥1700 |
|
|
Thermal Shock Resistance (1100°C, Water Cooling, Cycles)
|
≥10 |
|
|
Thermal Conductivity (1000°C, W/(m·K))
|
≤2.8 |
|
|
Main Use
|
Transition Zone & Burning Zone
|
|