- Home
- Products and Services
- Cement
- Product
Products and Services
- Cement
-
Metallurgy
-
Product
- Blast Furnace Ceramic Cup Series Shaped Products
- Blast Furnace Ceramic Cup Corundum-Silicon Nitride Precast Series Products
- Blast Furnace Ceramic Cup Supporting Slurry Series Products
- Blast Furnace Rapid Repair and Long-Life Series Products
- Refractory Materials for Blast Furnace Taphole
- Belt Roasting Machine Pellet Series Supporting Products
- Grate-Rotary Kiln Pellet Series Supporting Products
- Solutions
-
Product
- Environmental Protection
- Energy
- Aerospace
- Refractory Raw Materials
- Home
- Products and Services
- Cement
- Product
- Kiln Outlet
- New Cement-free Castable
New Cement-free Castable
【Product brand】ASM-A
【Recommended use】Kiln Outlet, Burner Pipe
Product Introduction
The product has the following characteristics:
(1) No pre-baking required, explosion-proof, fast demolding time, and no need for moisture curing.
(2) Ultra-low water addition, inorganic chemical bonding, and stable hardening.
(3) Achieves medium-temperature sintering, low dense porosity, high strength, good wear resistance, and excellent thermal shock stability.
(4) Workable time exceeds 30 minutes, fully hardens in 6 hours to demold, with optimal performance achieved one week after demolding.
Products Quality
|
Product Name |
New Cement-free Castable
|
|
|
Product Code
|
ASM-A |
|
|
Chemical Composition (%)
|
Al2O3 |
≥65 |
|
|
CaO |
≤0.5 |
|
Bulk Density (g/cm³)
|
110℃×24h
|
≥2.85 |
|
Modulus of Rupture (MPa)
|
110℃×24h
|
≥8 |
|
|
1100℃×3h
|
≥15 |
|
|
1400℃×3h
|
≥10 |
|
Cold Crushing Strength (MPa)
|
110℃×24h
|
≥50 |
|
|
1100℃×3h
|
≥100 |
|
|
1400℃×3h
|
≥80 |
|
Permanent Linear Change (%)
|
1100℃×3h
|
±0.2 |
|
|
1400℃×3h
|
±0.4 |
|
Abrasion Resistance (cc)
|
1100℃×3h
|
≤5.0 |
|
Thermal Shock Resistance (1100°C, Water Cooling, Cycles)
|
≥30 |
|
|
Main Use
|
Kiln Outlet, Burner Pipe
|
|