- Home
- Products and Services
- Cement
- Product
Products and Services
- Cement
-
Metallurgy
-
Product
- Blast Furnace Ceramic Cup Series Shaped Products
- Blast Furnace Ceramic Cup Corundum-Silicon Nitride Precast Series Products
- Blast Furnace Ceramic Cup Supporting Slurry Series Products
- Blast Furnace Rapid Repair and Long-Life Series Products
- Refractory Materials for Blast Furnace Taphole
- Belt Roasting Machine Pellet Series Supporting Products
- Grate-Rotary Kiln Pellet Series Supporting Products
- Solutions
-
Product
- Environmental Protection
- Energy
- Aerospace
- Refractory Raw Materials
- Home
- Products and Services
- Cement
- Product
- Other areas
- Rapid Hardening and High-...
Rapid Hardening and High-Strength Castable
【Product brand】GB-16K
【Recommended use】Kiln Hood, Grate Cooler
Product Introduction
Main Performance Characteristics:
(1) The product employs high-quality raw materials with strictly controlled matrix composition, resulting in enhanced high-temperature strength, excellent thermal shock stability, improved resistance to erosion and abrasion, and extended service life.
(2) This product features rapid hardening and high strength, meeting the needs for urgent repairs. It is preferentially recommended for use in areas such as kiln hoods and grate coolers.
Products Quality
|
Material Name Product Name |
Rapid Hardening and High-Strength Castable Rapid Hardening and High-Strength Castable |
|
|
Product Code Product Code |
GB-16K |
|
|
Chemical Composition (%) Chemical Composition |
Al2O3+SiO2 |
≥70 |
|
Bulk Density (g/cm³) Bulk Density |
110℃×24h 110 °C×24h |
≥2.50 |
|
Modulus of Rupture (MPa) Modulus of Rupture |
110℃×24h 110 °C×24h |
≥10 |
|
|
1100℃×3h 1100 °C×3h |
≥11 |
|
Cold Crushing Strength (MPa)
|
110℃×24h 110 °C×24h |
≥100 |
|
|
1100℃×3h 1100 °C×3h |
≥100 |
|
Permanent Linear Change (%)
|
1100℃×3h 1100 °C×3h |
±0.4 |
|
Abrasion Resistance (cc)
|
1100℃×3h 1100 °C×3h |
≤6.5 |
|
Main Use
|
Kiln Hood, Grate Cooler
|
|