- Home
- Products and Services
- Cement
- Product
Products and Services
- Cement
-
Metallurgy
-
Product
- Blast Furnace Ceramic Cup Series Shaped Products
- Blast Furnace Ceramic Cup Corundum-Silicon Nitride Precast Series Products
- Blast Furnace Ceramic Cup Supporting Slurry Series Products
- Blast Furnace Rapid Repair and Long-Life Series Products
- Refractory Materials for Blast Furnace Taphole
- Belt Roasting Machine Pellet Series Supporting Products
- Grate-Rotary Kiln Pellet Series Supporting Products
- Solutions
-
Product
- Environmental Protection
- Energy
- Aerospace
- Refractory Raw Materials
- Home
- Products and Services
- Cement
- Product
- Other areas
- Alkali Resistance and Abr...
Alkali Resistance and Abrasion Resistance Rapid Repair Materials
【Product brand】PA-902
【Recommended use】Kiln Hood, Kiln Outlet, Burner Pipe
Product Introduction
(1) The Alkali Resistance and Abrasion Resistance Rapid Repair Material PA-902 features no curing or baking requirements and is explosion-proof, allowing immediate ignition after construction, making it ideal for rapid repairs in cement kilns.
(2) It offers excellent alkali resistance and wear resistance, extending the service life of refractory materials in these areas.
Products Quality
|
Product Name |
Alkali Resistance and Abrasion Resistance Rapid Repair Materials
|
|
|
Product Code
|
PA-902 |
|
|
Chemical Composition (%)
|
Al2O3+SiO2 |
≥70 |
|
Bulk Density (g/cm³)
|
110℃×24h 110 °C×24h |
≥2.70 |
|
Modulus of Rupture (MPa)
|
110℃×24h 110 °C×24h |
≥8 |
|
|
1100℃×3h 1100 °C×3h |
≥12 |
|
|
1400℃×3h 1400 °C×3h |
≥12 |
|
Cold Crushing Strength (MPa)
|
110℃×24h 110 °C×24h |
≥45 |
|
|
1100℃×3h 1100 °C×3h |
≥70 |
|
|
1400℃×3h 1400 °C×3h |
≥90 |
|
Permanent Linear Change (%)
|
1100℃×3h 1100 °C×3h |
±0.4 |
|
|
1400℃×3h 1400 °C×3h |
±0.4 |
|
Main Use
|
Kiln Hood, Kiln Outlet, Burner Pipe
|
|